Table 2 A study examining Al corrosion inhibitors in the absence and presence of MOF1@TiO2 at 400 ppm and their effectiveness at different temperatures

From: Experimental and theoretical studies of the efficiency of metal–organic frameworks (MOFs) in preventing aluminum corrosion in hydrochloric acid solution

Conc., ppm

Temp.,oC

CR, mg/(cm2 min)

θ

η%

100

25

2.8 ± 0.001452

0.801

80.1

35

5.0 ± 0.001452

0.796

79.6

45

10.4 ± 0.08819

0.782

78.2

200

25

2.7 ± 0.001732

0.809

80.9

35

5.0 ± 0.001201

0.796

79.6

45

10.1 ± 0.00120

0.786

78.6

300

25

2.4 ± 0.00173

0.830

83.0

35

4.2 ± 0.002603

0.824

82.4

45

9 ± 0.010012

0.791

79.1

400

25

2.0 ± 0.00176

0.884

85.8

35

4.2 ± 0.00173

0.829

82.9

45

9.0.± 0.00120

0.812

81.2