Experimental and theoretical studies of the efficiency of metal–organic frameworks (MOFs) in preventing aluminum corrosion in hydrochloric acid solution

Table 1 An investigation of Al corrosion inhibitors activity at different temperatures in the presence and absence of MOF1

Conc., ppm	Temp.,^oC	CR, mg/(cm² min)	Θ*	η%
Blank	25	14.1 ± 0.4234	–	–
	35	24.5 ± 0.8232	–	–
	45	47.8 ± 0.9921	–	–
100	25	2.4 ± 0.001201	0.831	83.1
	35	5.1 ± 0.000881	0.796	79.6
	45	10.7 ± 0.002027	0.776	77.6
200	25	2.36 ± 0.001463	0.839	83.0
	35	4.9 ± 0.001154	0.800	80.0
	45	10.7 ± 0.001763	0.783	78.3
300	25	2.3 ± 0.001763	0.840	84.0
	35	5.2 ± 0.001452	0.803	80.3
	45	9.8 ± 0.001201	0.794	79.4
400	25	2.4 ± 0.00120	0.855	83.0
	35	5.1 ± 0.002081	0.806	80.6
	45	9.90.003511	0.794	79.4

ISSN: 2661-801X