Polym. no | Steps | T (°C) | % wt loss | Residue (%) | Td (°C) |
---|---|---|---|---|---|
52 | I | 20–385 | 43.05 | 0.24 | 307 |
II | 385–451 | 11.2 |  | 440 | |
III | 451–622 | 45.49 |  | 591 | |
53 | I | 20–497 | 45.05 | 1.67 | 493 |
II | 497–663 | 53.29 |  | 596 | |
54 | I | 20–340 | 28.19 | 3.05 | 315 |
II | 340–450 | 21.4 |  | 440 | |
III | 450–502 | 19.11 |  | 487 | |
IV | 502–590 | 28.26 |  | 540 | |
55 | I | 20–303 | 13.51 | 1.26 | 160 |
II | 303–411 | 19.27 |  | 371 | |
III | 411–647 | 65.96 |  | 592 | |
56 | I | 20–392 | 24.03 | 3.18 | 376 |
II | 392–566 | 53.3 |  | 560 | |
III | 566–629 | 19.5 |  | 587 | |
57 | I | 20–410 | 23.93 | 10.1 | 386 |
II | 410–528 | 21.0 |  | 492 | |
III | 528–600 | 12.9 |  | 559 | |
IV | 600–700 | 32.98 |  | 656 |