Sample | TM, °C | Weight loss %, in temperature intervals, °C | m\( _{{{\text{H}}_{2} {\text{O}}}} \), mmol g−1 | ||
---|---|---|---|---|---|
25–110 | 25–300 | 25–1000 | |||
N-CLI | 100 | 2.4 | 7.2 | 12.0 | 2.7 |
0.25H-CLI | 110 | 1.6 | 6.6 | 10.0 | 2.8 |
0.5H-CLI | 100 | 2.2 | 7.0 | 10.4 | 2.7 |
1H-CLI | 100 | 3.2 | 8.2 | 12.0 | 2.8 |
3H-CLI | 110 | 2.2 | 9.2 | 13.2 | 3.3 |
Pd(II)–Cu(II)/0.25H-CLI | 110 | 3.0 | 8.4 | 12.4 | 3.0 |
Pd(II)–Cu(II)/0.5H-CLI | 100 | 3.0 | 8.4 | 13.2 | 3.0 |
Pd(II)–Cu(II)/1H-CLI | 110 | 2.8 | 8.8 | 12.8 | 3.3 |
Pd(II)–Cu(II)/3H-CLI | 120 | 3.6 | 9.0 | 12.0 | 3.1 |